E819CA + D91 dviejų komponentų derva su priedu, polimerizacija vyksta kambario temperatūroje
  • E819CA + D91 dviejų komponentų derva su priedu, polimerizacija vyksta kambario temperatūroje

Nuotraukos yra skirtos tik informaciniams tikslams. Peržiūrėkite produkto specifikaciją

please use latin characters

Gamintojas: SEG

E819CA + D91 dviejų komponentų derva su priedu, polimerizacija vyksta kambario temperatūroje

Application:
 Half hard resin is used in electro technical and electronic industry.
- Electric material insulation,
- for electronic components flooding.

Main characteristic:
-  two component resin with good thermal conductance and compatible with insulation systems class F.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Packing:
- in containers 1, 5 and 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

Preliminary polymer part A Hardener part B
viscosity @ 23°C /Reomat NSEG0013 12 600±4 000mPas viscosity @  23°C /Reomat NSEG0013 680 ± 200 mPas
Volume weight ISO 2811   Volume weight ISO 2811 1,00 g/ml
Colour   brown Colour   yellow
Mixture A + B
Mixture weight ratio   100 /13 ± 1
Mixture volume ratio   100/17,7
Insert content   53%
viscosity @ 23°C /Reomat/ NSEG0013 1 800 ± 700 mPas
Volume weight ISO 2811 1,28 g/ml
lifetime 150g @ 23°C NSEG 0005 29 min
Gelation time @ 23° -150 g NSEG 0008 59 min
Gelation time @ 78°- 2,5 g NSEG 0012 7 min 30 s ± 3 min
Exothermic peak @50 g NSEG 0007 30 °C
Exothermic peak @ 100g NSEG 0007 30 °C
Exothermic peak @ 200g NSEG 0007 36 °C
 
Polymerisation
W20°C NSEG 0010  
W60°C NSEG 0010 45 min
 
Mechanical properties
Line shrinkage ISO 3521 < 1.0%
Stretch ISO R 527 210daN/cm2
Lengthen ISO R 527 <4%
Shore hardness A/D @ 23°C ISO 868 60 D
 
Electrical properties
Dielectric withstand CEI 243 20 kV/mm
Dielectric constant @ CEI 250 (50 Hz)
Tg d @ 23°C CEI 250 (50 Hz)
 
Thermal properties
Constant operation temperature   -40+155°C
Thermal conductance   0.60 ±0.1 W/m.°C
Glassy phase   41 °C
Self - extinguished SEG V0 6 mm
mažiau
Skaityk daugiau

Atsiųskite užklausą

Ar Jūs domina šis produktas? Ar Jums reikia papildomos informacijos ar individualaus pasiūlymo?

Susisiekite su mumis

KLAUSKITE PRODUKTO close
Pranešimas sėkmingai išsiųstas.
KLAUSKITE PRODUKTO close
Naršyti

Pridėti į norų sąrašą

tu turi būti prisijungęs

Application:
 Half hard resin is used in electro technical and electronic industry.
- Electric material insulation,
- for electronic components flooding.

Main characteristic:
-  two component resin with good thermal conductance and compatible with insulation systems class F.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Packing:
- in containers 1, 5 and 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

Preliminary polymer part A Hardener part B
viscosity @ 23°C /Reomat NSEG0013 12 600±4 000mPas viscosity @  23°C /Reomat NSEG0013 680 ± 200 mPas
Volume weight ISO 2811   Volume weight ISO 2811 1,00 g/ml
Colour   brown Colour   yellow
Mixture A + B
Mixture weight ratio   100 /13 ± 1
Mixture volume ratio   100/17,7
Insert content   53%
viscosity @ 23°C /Reomat/ NSEG0013 1 800 ± 700 mPas
Volume weight ISO 2811 1,28 g/ml
lifetime 150g @ 23°C NSEG 0005 29 min
Gelation time @ 23° -150 g NSEG 0008 59 min
Gelation time @ 78°- 2,5 g NSEG 0012 7 min 30 s ± 3 min
Exothermic peak @50 g NSEG 0007 30 °C
Exothermic peak @ 100g NSEG 0007 30 °C
Exothermic peak @ 200g NSEG 0007 36 °C
 
Polymerisation
W20°C NSEG 0010  
W60°C NSEG 0010 45 min
 
Mechanical properties
Line shrinkage ISO 3521 < 1.0%
Stretch ISO R 527 210daN/cm2
Lengthen ISO R 527 <4%
Shore hardness A/D @ 23°C ISO 868 60 D
 
Electrical properties
Dielectric withstand CEI 243 20 kV/mm
Dielectric constant @ CEI 250 (50 Hz)
Tg d @ 23°C CEI 250 (50 Hz)
 
Thermal properties
Constant operation temperature   -40+155°C
Thermal conductance   0.60 ±0.1 W/m.°C
Glassy phase   41 °C
Self - extinguished SEG V0 6 mm
mažiau