DIAPOL 509FG + C500 dviejų komponentų derva su įdėklu, polimerizacija vyksta kambario temperatūroje
  • DIAPOL 509FG + C500 dviejų komponentų derva su įdėklu, polimerizacija vyksta kambario temperatūroje

Nuotraukos yra skirtos tik informaciniams tikslams. Peržiūrėkite produkto specifikaciją

please use latin characters

Gamintojas: SEG

DIAPOL 509FG + C500 dviejų komponentų derva su įdėklu, polimerizacija vyksta kambario temperatūroje

Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.

Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C NSEG0013 3200 ± 50 mPas viscosity @ 23°C NSEG0013 000 ± 50 mPas
Volume weight ISO 2811 1,45 g/ml Volume weight ISO 2811 1,23 g/ml
Colour   black Volume weight   brown
Mixture A + B
Mixture weight ratio   100/16 ± 1
Mixture volume ratio   -
Insert content   -%
viscosity @ 23°C NSEG0013 4000 ± 1200 mPas
Volume weight ISO 2811 1.40 g/ml
lifetime  150 g @ 23°C NSEG 0005 10 min
Gelation time @ 23°C   45 do 60 min
Gelation time @ 50°C   25 do 30 min
Exothermic peak @ 50 g NSEG 0007 - °C
Exothermic peak @ 100 g NSEG 0007 - °C
Exothermic peak @ 5 kg NSEG 0007 42°C
 
Polymerization
W20°C NSEG 0010 8 h. 30 min
W60°C NSEG 0010 2 h. 30 min
 
Mechanical properties
Line shrinkage ISO 3521 < 0,5 %
Break off resistance ISO R 527 2
Lengthening during break off ISO R 527 <19%
Shore hardness A/D @ 23°C ISO 868 85 A
 
Electrical properties
Dielectric withstand CEI 243 >15kV/mm
Dielectric constant @ 23°C CEI 250 4,2 (50Hz)
Loss coefficient @  23°C CEI 250 0.04 (50Hz)
Resistivity 3*1013 Ω/cm
 
Thermal properties
Constant operation temperature   od-30°Cdo130°C
Thermal conductance   0,65 W/m.°C
Self - extinguished UL 94 V0 6mm

Atsiųskite užklausą

Ar Jūs domina šis produktas? Ar Jums reikia papildomos informacijos ar individualaus pasiūlymo?

Susisiekite su mumis

KLAUSKITE PRODUKTO close
Pranešimas sėkmingai išsiųstas.
KLAUSKITE PRODUKTO close
Naršyti

Pridėti į norų sąrašą

tu turi būti prisijungęs

Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.

Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C NSEG0013 3200 ± 50 mPas viscosity @ 23°C NSEG0013 000 ± 50 mPas
Volume weight ISO 2811 1,45 g/ml Volume weight ISO 2811 1,23 g/ml
Colour   black Volume weight   brown
Mixture A + B
Mixture weight ratio   100/16 ± 1
Mixture volume ratio   -
Insert content   -%
viscosity @ 23°C NSEG0013 4000 ± 1200 mPas
Volume weight ISO 2811 1.40 g/ml
lifetime  150 g @ 23°C NSEG 0005 10 min
Gelation time @ 23°C   45 do 60 min
Gelation time @ 50°C   25 do 30 min
Exothermic peak @ 50 g NSEG 0007 - °C
Exothermic peak @ 100 g NSEG 0007 - °C
Exothermic peak @ 5 kg NSEG 0007 42°C
 
Polymerization
W20°C NSEG 0010 8 h. 30 min
W60°C NSEG 0010 2 h. 30 min
 
Mechanical properties
Line shrinkage ISO 3521 < 0,5 %
Break off resistance ISO R 527 2
Lengthening during break off ISO R 527 <19%
Shore hardness A/D @ 23°C ISO 868 85 A
 
Electrical properties
Dielectric withstand CEI 243 >15kV/mm
Dielectric constant @ 23°C CEI 250 4,2 (50Hz)
Loss coefficient @  23°C CEI 250 0.04 (50Hz)
Resistivity 3*1013 Ω/cm
 
Thermal properties
Constant operation temperature   od-30°Cdo130°C
Thermal conductance   0,65 W/m.°C
Self - extinguished UL 94 V0 6mm