Vernis alkyd modifié G159, G159T

One component material, for electrical insulation class  B 130°C

Dry on air.

Application:
- electro technical material class B,
- transformers.

Main preferences
- Impregnation lacquer made from modified alkyd resin, dry fast on air, give good protection film
- resistant for humidity and mineral oils.
- is comptabile with cables in enamel class B, F and H,
- G 159 T (tropical version)satisfy requirements 41514 NFX.

Impregnation:
- by immersion, spray or vacuum.

Polymerisation:
- Few hours in a room temperature. After one hour lacquer is not viscous.
- lacquer preferences are better when it is dried in  temperature 80/100°C,
- whenn resistance for diluent or chemicals is needed, it must be dried in temperature 130°C.

Storage conditions:
6 months in original and closed package, far away from the sun and heat source.

Packing
- containers 1, 5, 30 l or 200 barrels and spray.

Hygiene and protection:
Lacquer consists ksylen.

Lacquer Standard G 159 G 159T
Chemical origins   Modified alkyd Modified alkyd
Thermal class   (B)/130°C (B)/130°C
viscosity ISO 2431 60s +/- 20s 60s +/- 20s
density @ 20°C NFT30020 0,95 0,95
Ignition point - crucible closed NFT 30020 26°C 26°C
Dry extract NSEG 0001 40% +/- 2 40% +/- 2
Colour   Mahoń, pomarańcz. Mahoń
Drying on a plate NSEG 0002 w 23°C 45 min. w23°C45 min.
Diluent   37022 37022

Preferences

Breakdown on a copper plate [thickness 0,01 mm] Volt
natural state 1000
After 8 days in humid air: 850
After 8 days in destilated water: 800
After 8 days in oil: 1200
Moins
Lire la suite

Envoyez une demande

Êtes-vous intéressé par ce produit? Avez-vous besoin d'informations supplémentaires ou d'une tarification individuelle?

Nous contacter

DEMANDEZ LE PRODUIT close
Message envoyé avec succès.
DEMANDEZ LE PRODUIT close
Feuilleter

Ajouter à la liste de souhaits

Vous devez être connecté

One component material, for electrical insulation class  B 130°C

Dry on air.

Application:
- electro technical material class B,
- transformers.

Main preferences
- Impregnation lacquer made from modified alkyd resin, dry fast on air, give good protection film
- resistant for humidity and mineral oils.
- is comptabile with cables in enamel class B, F and H,
- G 159 T (tropical version)satisfy requirements 41514 NFX.

Impregnation:
- by immersion, spray or vacuum.

Polymerisation:
- Few hours in a room temperature. After one hour lacquer is not viscous.
- lacquer preferences are better when it is dried in  temperature 80/100°C,
- whenn resistance for diluent or chemicals is needed, it must be dried in temperature 130°C.

Storage conditions:
6 months in original and closed package, far away from the sun and heat source.

Packing
- containers 1, 5, 30 l or 200 barrels and spray.

Hygiene and protection:
Lacquer consists ksylen.

Lacquer Standard G 159 G 159T
Chemical origins   Modified alkyd Modified alkyd
Thermal class   (B)/130°C (B)/130°C
viscosity ISO 2431 60s +/- 20s 60s +/- 20s
density @ 20°C NFT30020 0,95 0,95
Ignition point - crucible closed NFT 30020 26°C 26°C
Dry extract NSEG 0001 40% +/- 2 40% +/- 2
Colour   Mahoń, pomarańcz. Mahoń
Drying on a plate NSEG 0002 w 23°C 45 min. w23°C45 min.
Diluent   37022 37022

Preferences

Breakdown on a copper plate [thickness 0,01 mm] Volt
natural state 1000
After 8 days in humid air: 850
After 8 days in destilated water: 800
After 8 days in oil: 1200
Moins
Lire la suite