Zweikomponentenharz ohne JBR19.4 + D19.4, Polymerisation bei Umgebungstemperatur

Application:
-Half hard resin is used in electro technical and electronic industry..
Main characteristic:
- epoxide two component resin with good thermal conductance, compatible with insulation systems class F.

Polymerisation:
- polymerisation is complete after 47h in temperature 20°C,
- it is recommended to heat up for an hour to temperature 50C after polymerization to obtain optimal parameters.

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Storage conditions:
-6 months in original closed container, in temperature 10°C - 25 °C.

Packing:
- in containers 1, 5 i 20 kg and barrels 200 kg,
- part B is delivered in corresponding proportion to part A.

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C   624 mPas viscosity @ 23°C   19 mPas
Reomat 108 E/R speed 50s+1 Reomat 108 E/R   190s+1
Volume weight   1,09 g/ml Volume weight   0,89 g/ml
Colour   transparent     yellow
Mixture A + B
Mixture weight ratio   100/20
Mixture volume ratio   80/20
Insert content   0%
viscosity @ 23°C   855 mPas
Reomat 108 E/R speed 50s+1
Volume weight   1,06 g/ml
lifetime  150 g @ 23°C   106 min
Gelation time @ 121°C   3min ± 30s
Exothermic peak @ 50 g   27 °C
Exothermic peak @ 100 g   28 °C
Exothermic peak @ 200 g   35 °C
Polymerisation
W20°C   18 h
W100°C   1 h30 min
Mechanical properties
Line shrinkage ISO 3521 %
Break off resistance ISO R 527 157 daN/cm2
Lengthening during break off ISO R 527 48,7 %
Shore hardness A/D @ 23°C ISO 868 D61
 
Electrical properties
Dielectric withstand CEI 243 20 kV/mm
 
Thermal properties
Constant operation temperature   od-30 do 155 °C
Self - extinguished UL 94 no
Weniger
Weiterlesen

Senden Sie eine Anfrage

Interessieren Sie sich für dieses Produkt? Benötigen Sie zusätzliche Informationen oder individuelle Preise?

Kontaktiere uns

FRAGEN SIE NACH DEM PRODUKT close
Nachricht erfolgreich gesendet.
FRAGEN SIE NACH DEM PRODUKT close
Durchsuche

Zur Wunschliste hinzufügen

Sie müssen eingeloggt sein

Application:
-Half hard resin is used in electro technical and electronic industry..
Main characteristic:
- epoxide two component resin with good thermal conductance, compatible with insulation systems class F.

Polymerisation:
- polymerisation is complete after 47h in temperature 20°C,
- it is recommended to heat up for an hour to temperature 50C after polymerization to obtain optimal parameters.

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Storage conditions:
-6 months in original closed container, in temperature 10°C - 25 °C.

Packing:
- in containers 1, 5 i 20 kg and barrels 200 kg,
- part B is delivered in corresponding proportion to part A.

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C   624 mPas viscosity @ 23°C   19 mPas
Reomat 108 E/R speed 50s+1 Reomat 108 E/R   190s+1
Volume weight   1,09 g/ml Volume weight   0,89 g/ml
Colour   transparent     yellow
Mixture A + B
Mixture weight ratio   100/20
Mixture volume ratio   80/20
Insert content   0%
viscosity @ 23°C   855 mPas
Reomat 108 E/R speed 50s+1
Volume weight   1,06 g/ml
lifetime  150 g @ 23°C   106 min
Gelation time @ 121°C   3min ± 30s
Exothermic peak @ 50 g   27 °C
Exothermic peak @ 100 g   28 °C
Exothermic peak @ 200 g   35 °C
Polymerisation
W20°C   18 h
W100°C   1 h30 min
Mechanical properties
Line shrinkage ISO 3521 %
Break off resistance ISO R 527 157 daN/cm2
Lengthening during break off ISO R 527 48,7 %
Shore hardness A/D @ 23°C ISO 868 D61
 
Electrical properties
Dielectric withstand CEI 243 20 kV/mm
 
Thermal properties
Constant operation temperature   od-30 do 155 °C
Self - extinguished UL 94 no
Weniger