Two component resin with insert DIAPOL 509FG + C500,- polymerization in an room temperature
  • Two component resin with insert DIAPOL 509FG + C500,- polymerization in an room temperature

Photos are for informational purposes only. View product specification

please use latin characters

Manufacturer: SEG

Two-component resin with DIAPLOL 509FG + C500, polymerization at room temperature

Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.

Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C NSEG0013 3200 ± 50 mPas viscosity @ 23°C NSEG0013 000 ± 50 mPas
Volume weight ISO 2811 1,45 g/ml Volume weight ISO 2811 1,23 g/ml
Colour   black Volume weight   brown
Mixture A + B
Mixture weight ratio   100/16 ± 1
Mixture volume ratio   -
Insert content   -%
viscosity @ 23°C NSEG0013 4000 ± 1200 mPas
Volume weight ISO 2811 1.40 g/ml
lifetime  150 g @ 23°C NSEG 0005 10 min
Gelation time @ 23°C   45 do 60 min
Gelation time @ 50°C   25 do 30 min
Exothermic peak @ 50 g NSEG 0007 - °C
Exothermic peak @ 100 g NSEG 0007 - °C
Exothermic peak @ 5 kg NSEG 0007 42°C
 
Polymerization
W20°C NSEG 0010 8 h. 30 min
W60°C NSEG 0010 2 h. 30 min
 
Mechanical properties
Line shrinkage ISO 3521 < 0,5 %
Break off resistance ISO R 527 2
Lengthening during break off ISO R 527 <19%
Shore hardness A/D @ 23°C ISO 868 85 A
 
Electrical properties
Dielectric withstand CEI 243 >15kV/mm
Dielectric constant @ 23°C CEI 250 4,2 (50Hz)
Loss coefficient @  23°C CEI 250 0.04 (50Hz)
Resistivity 3*1013 Ω/cm
 
Thermal properties
Constant operation temperature   od-30°Cdo130°C
Thermal conductance   0,65 W/m.°C
Self - extinguished UL 94 V0 6mm

Send an inquiry

Are you interested in this product? Do you need additional information or individual pricing?

Contact us

ASK FOR THE PRODUCT close
Message sent successfully.
ASK FOR THE PRODUCT close
Browse

Add to Wishlist

You must be logged in

Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.

Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.

Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature  10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..

 
Preliminary polymer part A Hardener part B
viscosity @ 23°C NSEG0013 3200 ± 50 mPas viscosity @ 23°C NSEG0013 000 ± 50 mPas
Volume weight ISO 2811 1,45 g/ml Volume weight ISO 2811 1,23 g/ml
Colour   black Volume weight   brown
Mixture A + B
Mixture weight ratio   100/16 ± 1
Mixture volume ratio   -
Insert content   -%
viscosity @ 23°C NSEG0013 4000 ± 1200 mPas
Volume weight ISO 2811 1.40 g/ml
lifetime  150 g @ 23°C NSEG 0005 10 min
Gelation time @ 23°C   45 do 60 min
Gelation time @ 50°C   25 do 30 min
Exothermic peak @ 50 g NSEG 0007 - °C
Exothermic peak @ 100 g NSEG 0007 - °C
Exothermic peak @ 5 kg NSEG 0007 42°C
 
Polymerization
W20°C NSEG 0010 8 h. 30 min
W60°C NSEG 0010 2 h. 30 min
 
Mechanical properties
Line shrinkage ISO 3521 < 0,5 %
Break off resistance ISO R 527 2
Lengthening during break off ISO R 527 <19%
Shore hardness A/D @ 23°C ISO 868 85 A
 
Electrical properties
Dielectric withstand CEI 243 >15kV/mm
Dielectric constant @ 23°C CEI 250 4,2 (50Hz)
Loss coefficient @  23°C CEI 250 0.04 (50Hz)
Resistivity 3*1013 Ω/cm
 
Thermal properties
Constant operation temperature   od-30°Cdo130°C
Thermal conductance   0,65 W/m.°C
Self - extinguished UL 94 V0 6mm