Double-component resin U4612 + D84-15, polymerization at ambient temperature

Application:
Elastic resin, for electronic and electro technical industry usage.
- electrical devices insulation,
- drowning electrical components,
- doesn't react with electronic components.

Obtain an ambient temperature for 48h before usage. .

Main characteristic:
- polyurethane resin has good thermal conductance.
- compatible with insulation class B,
- it is also possible to use red hardener. D 84-15(R)

Polymerisation (NSEG0010):
- @ 20°C: 9 h,
- @ 60°C: 2 h.
polymerisation can be fastened in the drier(60C max temperature)

Storage conditions:
6 months in original, closed container, temperature: 10°C - 30°C.
Product sensitive for humidity!

Packing:
- in containers 1, 5 i 20 kg and barrels 200 kg,
- part B is delivered in corresponding proportion to part A..

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

 
Preliminary polymer Part A Hardener part B
viscosity @ 23°C NSEG0013 20000mPas viscosity @23°C NSEG0013 215mPas
weight ISO2811 10,99 g/ml weight ISO2811 0,99 g/ml
Colour   natural
Colour
  without colour
Mixture A + B
Mixture weight ratio   100/15
Mixture volume ratio   80/20
Insert content   54 %
viscosity @ 23°C  NSEG0013 6000 mPas
Volume weight ISO2811 1,55 g/ml
lifetime 150 g @ 23°C NSEG0005 25s
Gelation time @ 33°C - 110 g NSEG0008 19s ± 6s
Gelation time @ 43°C - 110 g NSEG0012 -
Exothermic peak @ 50 g NSEG0007 23°C
Exothermic peak @ 100 g NSEG0007 25°C
Mechanical properties
Line shrinkage ISO3521 < 0,5 %
Break off resistance ISOR527 7,5 daN/cm2
Lengthening during break off ISOR527 168%
 Shore hardness A/D @ 23°C ISO868 A 20
 
Electrical properties
Dielectric withstand CEI243 22 kV/mm
Dielectric constant @ 23°C (50 Hz) CEI250 3,30
Loss coefficient @ 23°C (50 Hz) CEI250 0,125
Thermal properties
Constant operation temperature   -50°C do125°C
Thermal conductance   0,400 W/m.°C
Self - extinguished UL94 no

Send an inquiry

Are you interested in this product? Do you need additional information or individual pricing?

Contact us

ASK FOR THE PRODUCT close
Message sent successfully.
ASK FOR THE PRODUCT close
Browse

Add to Wishlist

You must be logged in

Application:
Elastic resin, for electronic and electro technical industry usage.
- electrical devices insulation,
- drowning electrical components,
- doesn't react with electronic components.

Obtain an ambient temperature for 48h before usage. .

Main characteristic:
- polyurethane resin has good thermal conductance.
- compatible with insulation class B,
- it is also possible to use red hardener. D 84-15(R)

Polymerisation (NSEG0010):
- @ 20°C: 9 h,
- @ 60°C: 2 h.
polymerisation can be fastened in the drier(60C max temperature)

Storage conditions:
6 months in original, closed container, temperature: 10°C - 30°C.
Product sensitive for humidity!

Packing:
- in containers 1, 5 i 20 kg and barrels 200 kg,
- part B is delivered in corresponding proportion to part A..

Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

 
Preliminary polymer Part A Hardener part B
viscosity @ 23°C NSEG0013 20000mPas viscosity @23°C NSEG0013 215mPas
weight ISO2811 10,99 g/ml weight ISO2811 0,99 g/ml
Colour   natural
Colour
  without colour
Mixture A + B
Mixture weight ratio   100/15
Mixture volume ratio   80/20
Insert content   54 %
viscosity @ 23°C  NSEG0013 6000 mPas
Volume weight ISO2811 1,55 g/ml
lifetime 150 g @ 23°C NSEG0005 25s
Gelation time @ 33°C - 110 g NSEG0008 19s ± 6s
Gelation time @ 43°C - 110 g NSEG0012 -
Exothermic peak @ 50 g NSEG0007 23°C
Exothermic peak @ 100 g NSEG0007 25°C
Mechanical properties
Line shrinkage ISO3521 < 0,5 %
Break off resistance ISOR527 7,5 daN/cm2
Lengthening during break off ISOR527 168%
 Shore hardness A/D @ 23°C ISO868 A 20
 
Electrical properties
Dielectric withstand CEI243 22 kV/mm
Dielectric constant @ 23°C (50 Hz) CEI250 3,30
Loss coefficient @ 23°C (50 Hz) CEI250 0,125
Thermal properties
Constant operation temperature   -50°C do125°C
Thermal conductance   0,400 W/m.°C
Self - extinguished UL94 no